Détails de la société
  • Torich International Co.,Ltd--The Steel Tube Maker

  •  [Zhejiang,China]
  • Type d'Affaires:Distributeur / Grossiste , Fabricant , Service , Société de commerce
  • Main Mark: Afrique , Amériques , Asie , Caraïbes , Europe de l'Est , L'Europe  , moyen-Orient , Europe du Nord , Océanie , Autres marchés , Europe occidentale , À l'échelle mondiale
  • Exportateur:31% - 40%
  • certs:GB, ISO9001, ISO14001
  • La description:GB 9948 tubes en acier sans soudure,12CrMo 15CrMo 12Cr1MoV 07Cr19Ni10,Tubes en acier sans soudure de craquage de pétrole
Torich International Co.,Ltd--The Steel Tube Maker GB 9948 tubes en acier sans soudure,12CrMo 15CrMo 12Cr1MoV 07Cr19Ni10,Tubes en acier sans soudure de craquage de pétrole
Accueil > Liste de Produits > Tubes en acier sans soudure > GB 9948 pétrole fissuration des tubes en acier sans soudure

GB 9948 pétrole fissuration des tubes en acier sans soudure

Partager sur:  
    Type de paiement: L/C,T/T,D/P,Paypal,Money Gram,Western Union
    Incoterm: FOB,CFR,CIF,FCA,CPT
    Quantité de commande minimum: 5 Ton
    Délai de livraison: 30 jours

Informations de base

Modèle: GB 9948

Additional Info

Détails d'emballage: emballage dans des boîtes en bois ou dans des paquets hexagonaux

productivité: 20000 Tons per Year

marque: Torich

transport: Ocean,Land,Air

Lieu d'origine: Chine

Capacité d'approvisionnement: 60000 Ton per year

Certificats : ISO9001:2008 ISO14001:2008, TS16949, CE PED, TUV, API

Code SH: 7304293000

Hafen: Shanghai,Ningbo

Description du produit

Nom du produit: GB 9948 Material10 # 20 # 12CrMo 15CrMo 12Cr1MoV Petroleum fissuration des tubes en acier sans soudure

Nous sommes fabricant de tubes en acier sans soudure en Chine, si vous voulez acheter Tube en acier au carbone sans soudure, Tube en acier à cylindre d'huile, Tube en acier sans soudure de précision, Tube en acier hydraulique Cylindre, veuillez nous contacter.

Diamètre extérieur: 3 ~ 600mm

Épaisseur de paroi: 0.5 ~ 50mm

Application: Il est employé pour les tubes en acier sans couture pour le four, les échangeurs de chaleur craquage de pétrole etc.



Tableau 1 Tolérances du diamètre extérieur et de l'épaisseur de paroi : mm

Sort Code

Manufacuring Method

Nominal Size

Tolerances

Common Level

High Level

W-H

Hot Rolling (Extrusion)

Outer Diameter     D

54

±0.50

±0.30

54~325

±1%D

±0.75%D

325

±1%D

-

Wall Thicknass     S

20

+15%S

-10%S

±10%S

20

+12.5%S

-10%S

±10%S

Hot Expand

Outer Diameter     D

All

±1%D

Wall Thicknass     S

All

±15%S

W-C

Cold Drawn(Rolling)

Outer Diameter     D

25.4

±0.15

25.4~40

±0.20

40~50

±0.25

50~60

±0.30

60

±0.75%D

±0.5%D

Wall Thicknass     S

3.0

±0.3

±0.2

3.0

±10%S

±7.5%S

Tableau 2 Tolérance de l'épaisseur minimale de paroi: mm

Sort Code

Manufacturing Method

Minimum Wall Thickness    Smin

Tolerance

Common Level

High Level

W-H

Hot Rolling(Extrusion)

4.0

+0.90

0

+0.70

0

4.0

+25%Smin

0

+22%Smin

0

W-C

Cold Drawn(Rolling)

3.0

+0.6

0

+0.4

0

3.0

+20%Smin

0

+15%Smin

0

Table3 Catégorie d'acier et composition chimique

Steel grade

Chemical composition %

C

Si

Mn

Cr

Mo

Ni

Nb

Ti

V

Cu

P

S

10

0.07~

0.13

0.17~

0.37

0.35~

0.65

0.15

0.15

0.25

-

-

0.08

0.20

0.025

0.015

20

0.17~

0.23

0.17~

0.37

0.35~

0.65

0.25

0.15

0.25

-

-

0.08

0.20

0.025

0.015

12CrMo

0.08~

0.15

0.17~

0.37

0.40~

0.70

0.40~

0.70

0.40~

0.55

0.30

-

-

-

0.20

0.025

0.015

15CrMo

0.12~

0.018

0.17~

0.37

0.40~

0.70

0.80~

1.10

0.40~

0.55

0.30

-

-

-

0.20

0.025

0.015

12CrlMo

0.08~

0.15

0.50~

1.00

0.30~

0.60

1.00~

1.50

0.45~

0.65

0.30

-

-

-

0.20

0.025

0.015

12CrlMoV

0.08~

0.15

0.17~

0.37

0.40~

0.70

0.90~

1.20

0.25~

0.35

0.30

-

-

0.15~

0.30

0.20

0.025

0.015

12Cr2Mo

0.08~

0.15

0.50

0.40~

0.60

2.00~

2.50

0.90~

1.13

0.30

-

-

-

0.20

0.025

0.015

12Cr5MoI

12Cr5MoNT

0.15

0.50

0.30~

0.60

4.00~

6.00

0.45~

0.60

0.60

-

-

-

0.20

0.025

0.015

12Cr9MoI

12Cr9MoNT

0.15

0.25~

1.00

0.30~

0.60

8.00~

10.00

0.90~

1.10

0.60

-

-

-

0.20

0.025

0.015

07Cr19Ni10

0.04~

0.10

1.00

2.00

18.00~

20.00

-

8.00~

11.00

-

-

-

-

0.030

0.015

07Cr18Ni11Nb

0.04~

0.10

1.00

2.00

17.00~

19.00

-

9.00~

12.00

8C~

1.10

-

-

-

0.030

0.015

07Cr19Ni11NTi

0.04~

0.10

0.75

2.00

17.00~

20.00

-

9.00~

13.00

-

4C~

0.60

-

-

0.030

0.015

022Cr17Ni12Mo2

0.30

1.00

2.00

16.00~

18.00

2.00~

3.00

10.00~

14.00

-

-

-

-

0.030

0.015

Tableau4 Norme de traitement thermique

Steel Grade

Heat Treatment Standard

10a

Normalizing;At Temperature 880℃~940℃

20a

Normalizing:At Temperature 880℃~940℃

12CrMob

Normalizing:At Temperature 900℃~960℃

Tempering:At Temperature 670℃~730℃

15CrMob

Normalizing:At Temperature 900℃~960℃

Tempering:At Temperature 680℃~730℃

12Cr1Mob

Normalizing:At Temperature 900℃~960℃

Tempering:At Temperature 680℃~750℃

12Cr1MoVb

S30mm:Normalizing:At Temperature 980℃~1020℃

Tempering:At Temperature 720℃~760℃

S30mm:Quenching:At Temperature 950℃~990℃

Tempering:At Temperature 720℃~760℃

Or       Normalizing:At Temperature 980℃~1020℃

(rapid cooling after Normalizing)

Tempering:At Temperature 720℃~760℃

12Cr2Mob

S30mm:Normalizing:At Temperature 900℃~960℃

Tempering:At Temperature 700℃~750℃

S30mm:Quenching:At Temperature ≥ 900℃

Tempering:At Temperature 700℃~750℃

Or       Normalizing:At Temperature 900℃~960℃

(rapid cooling after Normalizing)

Tempering:At Temperature 700℃~750℃

12Cr5MoI

Full Annealing or isothermal annealing

12Cr5MoNT

Normalizing:At Temperature 930℃~980℃

Tempering:At Temperature 730℃~770℃

12Cr9MoI

Full Annealing or isothermal annealing

12Cr9MoNT

Normalizing:At Temperature 890℃~950℃

Tempering:At Temperature 720℃~800℃

07Cr19Ni10

Treatment with solid solving:At Temperature ≥ 1040℃

(rapid cooling after Treatment)

 

07Cr18Ni11Nb

Treatment with solid solving:

For Hot Rolled Tube At Temperature ≥ 1050℃

For Cold Drawn(rolled)Tube At Temperature ≥ 1100℃

(rapid cooling after Treatment)

 

07Cr19Ni11Ti

Treatment with solid solving:

For Hot Rolled Tube At Temperature ≥ 1050℃

For Cold Drawn(rolled)Tube At Temperature ≥ 1100℃

(rapid cooling after Treatment)

 

Table5 Propriété mécanique

Steel Grade

Tensile

Strength

Rm/MPa

Lower yield strength Rp0.2/MPa

Elongation A/%

Shock absorption KV2/J

Brinell hardness

Longitudinal direction

Transverse

Longitudinal direction

Transverse

10

335~475

205

25

23

40

27

-

20

410~550

245

24

22

40

27

-

12CrMo

410~560

205

21

19

40

27

156HBW

15CrMo

440~640

295

21

19

40

27

170HBW

12Cr1Mo

415~560

205

22

20

40

27

163HBW

12Cr2MoV

470~640

255

21

19

40

27

179HBW

12Cr2Mo

450~600

280

22

20

40

27

163HBW

12Cr5MoI

415~590

205

22

20

40

27

163HBW

12Cr5MoNT

480~640

280

20

18

40

27

-

12Cr9MoI

460~640

210

20

18

40

27

179HBW

12Cr9MoNT

590~740

390

18

16

40

27

-

07Cr19Ni10

≥520

205

35

-

-

187HBW

07Cr18Ni11Nb

≥520

205

35

-

-

187HBW

07Cr19Ni11Ti

≥520

205

35

-

-

187HBW

022Cr17Ni12Mo2

≥485

170

35

-

-

187HBW

If the wall thickness of the tube is less than 5mm, doesn`t have to do the hardness test

Tableau 6 Facteur d'atténuation d'absorption d'énergie de choc de petit échantillon

Specimen

Specimen size(heightXwidth)mm

Attenuation factor

Standard sample

10X10

1.00

Small sample

10X7.5

0.75

Small sample

10X5

0.50

Table7 Diamètre d'évasement des tubes en acier

Steel

Diameter flaring rate of steel tubes/%

ID/OD

0.6

0.6~0.8

0.8

Carbon structural steel

10

12

17

Alloy structural steel

8

10

15

Stainless(heat resistance)steel

12

15

20

Tableau8 Éléments d'essai et quantité d'échantillonnage des tubes d'acier

Number

Testing items

Sampling quantity

1

Chemical composition

1 sample from each furnace

2

Tensile test

1 sample from each of two steel tubes on each batch

3

Hardness test

3 samples taken on 2 steel tubes on each batch

4

Impact test

All

5

Hydraulic test

1 sample from each of two steel tubes on each batch

6

Flattening test

2 samples taken on 2 steel tubes on each batch

7

Bending test

1 sample taken on 2 steel tubes on each furnace

8

Flaring test

2 samples taken on 2 steel tubes on each batch

9

Macroscopic examination

1 sample taken on 2 steel tubes on each furnace

10

Non-metallic inclusions

1 sample taken on 2 steel tubes on each furnace

11

Eddy current testing

All

12

Magnetic flux leakage detection 

All

13

Ultrasonic testing

All

14

Intergranular corrosion test

1 sample from each of two steel tubes on each batch

Tableau A.1 Tableau comparatif de la nuance d'acier similaire

No.

GB

Similar Steel Grade

ISO

EN

ASTM/ASME

JIS

1

10

-

P195GH

A

STB 340

2

20

PH26

P235GH

A-1.B

STB 410

3

12CrMo

-

-

T2/P2

STBA 20

4

15CrMo

13CrMo4-5

13CrMo4-5

T12/P12

STBA 22

5

12Cr1Mo

-

10CrMo5-5

T11/P11

STBA 23

6

12Cr1MoV

-

-

-

-

7

12Cr2Mo

10CrMo9-10

10CrMo9-10

T22/P22

STBA 24

8

12Cr5Mo-I

X11CrMo9-1TA

X11CrMo5+I

T5/P5

STBA 25

9

12Cr5Mo-NT

-

X11CrMo5+NT

T5/P5

STBA 25

10

12Cr9Mo-I

X11CrMo9-1TA

X11CrMo9-1+I

T9/P9

STBA 26

11

12Cr9Mo-NT

-

X11CrMo9-1+NT

T9/P9

STBA 26

12

07Cr19Ni10

X7CrNi18-9

X6CrNi18-10

TP304H

SUS 304H TB

13

07Cr18Ni11Nb

X7CrNiNb18-10

X7CrNiNb18-10

TP347H

SUS 347H TB

14

07Cr19Ni11Ti

-

X6CrNiTi18-10

TP321H

SUS 321H TB

15

022Cr17Ni12Mo2

-

X2CrNiMo17-12-2

TP316L

SUS 316L TB

Seamless Steel Tubes,Seamless Carbon Steel Tube,Oil Cylinder Steel Tube,Precision Seamless Steel Tube,Hydraulic Cylinder Steel Tube


Groupes de Produits : Tubes en acier sans soudure

image de Produit
  • GB 9948 pétrole fissuration des tubes en acier sans soudure
  • GB 9948 pétrole fissuration des tubes en acier sans soudure
  • GB 9948 pétrole fissuration des tubes en acier sans soudure
  • GB 9948 pétrole fissuration des tubes en acier sans soudure
  • GB 9948 pétrole fissuration des tubes en acier sans soudure
Envoyer à ce fournisseur
  • *Sujet:
  • *Messages:
    Votre message doit comporter de 20 à 8000 caractères

Site Web mobile Index. Plan du site


Abonnez-vous à notre newsletter:
Recevez des nouvelles, Offres spéciales, Big Prix, Réductions

MultiLanguage:
Copyright © 2018 Torich International Co.,Ltd--The Steel Tube MakerTous droits réservés.
Contacter le Fournisseur?fournisseur
Richard SHEN Mr. Richard SHEN
Que puis-je faire pour vous?
T'Chat contacter le fournisseur